Rev. 01/2017 titanium
Dedacciai K-19 titanium tubing constitute a large family of high performance products. titanium 2
They are manufactured in Ti-3Al-2.5V titanium grade, commonly named GR.9, Ti-6Al-4V, commonly named Gr.5, and Gr.2 titanium grade, in accordance with ASTM B338 rules. 9 is preferred for the most structural stressed tubing of the frame, meanwhile grade 2 grade is used where ductility and workability are the more important aspect. All the tubing are seamless, cold drawn and stress relieved (CWSR). To obtain the best results from the use of this class of products, please look carefully at the drawings, and read the advices at the end of this catalogue. 3
Titanium top tubing Ø31.7 Ø31.7 cod : MTO317T101 245 g 620.0 Ø34.9 Ø34.9 100.0 50.0 320.0 50.0 100.0 cod : MTO349T103 240 g - Cyclocross - MTB 620.0 titanium 4
59.5 Titanium down tubing Ø38.1 650.0 Ø38.1 cod : MTQ381T101 330 g - Cyclocross Ø41.5 100.0 50.0 350.0 50.0 100.0 Ø41.5 cod : MTQ415T105 320 g - Cyclocross 650.0 35 48 100.0 50.0 350.0 50.0 100.0 36 47 cod : MTQ415T101 320 g 650.0 Ø44 750.0 Ø44 cod : MTQ440T101 430 g - Cyclocross - MTB 34 53 750.0 Ø44 cod : MTQ440T102 430g - Cyclocross - MTB Ø48 670.0 Ø48 cod : MTQ480T101 440 g - Cyclocross - MTB 35 59.5 Ø48 cod : MTQ480T102 440 g - Cyclocross - MTB 670.0 35 59.5 35 cod : MTQ480T103 440 g - Cyclocross - MTB 670.0 5
Titanium seat tubing Aluminium sleeve to be glued Ø31.7 cod : MTV317T101 Ø31.7 Ø27.4 80.0 620 245 g Aluminium sleeve to be glued Ø35 Ø31.7 100 Ø35.3 0.85 280 60 660 60 0.85 60 Ø35 non tagliare don't cut cod : MTV350T102 285 g - Cyclocross - MTB Aluminium sleeve to be glued Ø35 Ø31.7 100 Ø35.3 0.85 280 60 60 160 0.85 60 Ø35 non tagliare don't cut cod : MTV350T103 285 g MTB titanium 6
5 6 Titanium chain stay 24.5 19.0 24.5 19.0 Ø22.2 Ø22.2 150.0 185.0 25.0 415.0 SIDE VIEW cod : MPO222T101 125 g 29.0 19.0 100.0 29.0 175.0 19.0 Ø24 170.0 165.0 25.0 Ø24 SIDE VIEW cod : MPO240T101 Ti Gr.2 120 g 420.0 170.0 28.5 18.5 18.5 28.5 SIDE VIEW cod : MPO240T105 Ti Gr.2 145 g 450.0 200 335 R220 28.5 12 18.5 TOP VIEW cod : MPO240T106 Ti Gr.2 145 g Cyclocross R220 335 R220 15 28.5 18.5 TOP VIEW cod : MPO240T104 Ti Gr.2 145 g MTB 29" 200 335 15 28.5 18.5 TOP VIEW cod : MPO240T103 Ti Gr.2 145 g MTB 29" 7
8 8 6 6 Titanium seat stay 5 cod : MPV160T101 Ti Gr.2 95 g 560.0 75.0 R150 5 375.0 R150 TOP VIEW cod : MPV160T102 Ti Gr.2 95 g 5 205.0 335.0 R150 12 TOP VIEW cod : MPV160T106 Ti Gr.2 95 g Cyclocross R230 220.0 5 370.0 R150 21 TOP VIEW cod : MPV160T105 Ti Gr.2 95 g Gravel - MTB 29" R220 265.0 0.8 bend center 80.0 155 R80.0 265.0 bend center 20 TOP VIEW SIDE VIEW cod : MPV160T104 Ti Gr.2 95 g MTB 29" cod : MPV160T103 105 g 560.0 titanium 8
8 8 12 Titanium seat stay Ø14 Ø19 cod : MPV190T101 150 Ti Gr.2 110 g 560.0 Ø14 205.0 335.0 R150 Ø19 cod : MPV190T106 Ti Gr.2 110 g Cyclocross R230 Ø14 cod : MPV190T103 220.0 370.0 R150 21 Ø19.0 Ti Gr.2 110 g Gravel - MTB 29" R220 9
Titanium spare parts Ø45 Ø42 Ø6.2 60.5 13 13 Ø37 Ø45 Alloy cup remove anodization before gluing 6 45 3 5.5 Ø45 Ø40 Ø10 1.25 1.25 255 20 68.5 SIDE VIEW 20 60 Ø10 27.1 20 Ø56 BSA THREAT FRONT VIEW 33.5 Ø56 Alloy cup remove anodization before gluing 45 2 Ø47 7.3 9.8 Ø52 Ø56 cod : MTSK19T56WOC Ti Gr.2 cod : MTSK19T56 Ti Gr.2 245 g 260 g cod : MBS4008KZ 95 g cod : FCRIBDTIT Ti Gr.5 70 g cod : PONTFRTIT Ti Gr.5 14 g - Cyclocross - MTB - Cyclocross - MTB - Cyclocross - MTB - Cyclocross - MTB Ø8 titanium 10
Chemical composition of Gr.9 (Ti-3Al-2.5V) titanium grade % Ti Balance Al 2.5-3.5 V 2.0-3.0 N < 0.02 C < 0.05 H < 0.015 Fe < 0.03 O < 0.12 All others < 0.4 (total) / < 0.1 (each) Typical Mechanical properties of Gr.9 tubing: Butted tubing: Ultimate strength > 850 Mpa (Best value 930 Mpa) Yield strength 790 Mpa Elongation % > 35 % Plain gauge tubing: Ultimate strength 680 Mpa Yield strength 620 Mpa Elongation % > 35 % Structural analysis data: Density 4.51 g/cm3 Modulus of Elasticity 103 GPa Yield strength 620 MPa 11
Chemical composition of Gr.5 (Ti-6Al-4V) titanium grade % Ti Balance Al 5.5-6.75 V 3.5-4.5 N < 0.05 C < 0.10 H < 0.0125 Fe < 0.30 O < 0.20 All others < 0.4 (total) / < 0.1 (each) Typical Mechanical properties of Gr.5 tubing: Plain gauge tubing / plates: Ultimate strength 900 Mpa Yield strength 830 Mpa Elongation % > 19 % Structural analysis data: Density 4.43 g/cm3 Modulus of Elasticity 120 GPa Yield strength 830 MPa titanium 12
Chemical composition of Gr.2 (Ti) titanium grade% Ti Balance N < 0.03 C < 0.10 H < 0.015 Fe < 0.30 O < 0.25 All others < 0.4 (total) / < 0.1 (each) Typical mechanical properties of Gr.2 tubing: Butted tubing: Ultimate strength > 620 Mpa (Best value 710 Mpa) Yield strength > 490 Mpa Elongation % > 30 Plain gauge tubing: Ultimate strength > 500 Mpa Yield strength 375 min / 400 Max Mpa Elongation % > 35 Structural analysis data: Density 4.43 g/cm3 Modulus of Elasticity 103 GPa Yield strength 375 MPa 13
Assembling of the tubing Geometrical features All the Dedacciai tubes and tube sets are designed for assembling frames based on current UCI geometry. In the choice of tubing for manufacturing a frames, please keep into account the following safety rules : Verify that for the selected geometry you will save a butt length longer than the thermal affected zone, and in any case longer that the tube diameter. If the butt length of down and top tubing butts are not symmetrical, pay attention in the tube orientation : at the head tube joint the tube must be only mitred, and not cutted. Depending on geometry, it is always better to keep top and down tubing spaced on head tube. Over imposed tubing geometries are less safe. recommended tubing can t be used for offroad frames. Fixing point and welding cordons closure points can give origin to fatigue cracks, realize them in the less stressed areas of the joints. It is recommended to completely weld the seat tube on bottom bracket, and then all other tubing. Top tube and seat stays must be approximately aligned at the seat tube joint. If you want to weld the seat stays below the top tube center line, please use the low geometry (LG) seat tubing (not available in the titanium set) Do not grind and/or polish the welding cordons. The risk of reducing the tube wall thickness is too high! titanium 14
Welding and post-welding advices Before welding the tubing, carefully clean them and remove dirty and grease inside and outside of the tube in the area to be jointed. The surfaces must be smooth and without notches. After mechanical cleaning, use acetone or MEK. Do not use chlorinated solvents. The suggested welding wire is Gr.5, (AWS classification ERti-5) Also the welding wire surface state is very important: stock it in clean areas, clean it before use and handle tubing and welding wire with gloves. During the welding process any area that will exceed 400 C must be shield from atmosphere contamination. Localized inert gas shielding or vacuum chamber is needed. 15